| Technical Data: | ||
Property | Test Method | Stantard |
| Tensile Strength(MPa) | ASTM D2671 | ≥14 |
| Elongation at Brealk | ASTM D2671 | ≥200 |
| Longitudinal shrink ratio | .224 | ≤±10% |
| Volume Resistance | ASTM D876 | ≥1×1014 |
| Flame Resistance | .224 | Outer layer is self-extinct |
| Copper stability 158℃,168hrs | .224 | Pass |
| Water Absorption | ASTM D570 | ≤0.5% |
| Hot Melting Adhesive Property | ||
Property | Test Method | Stantard |
| Water Absorption | ASTM-D570 | <0.2% |
| Vicat Softening Point | ASTM-E8 | 95℃ |
| Peel Strength(PE) | ASTM-D1000 | 120N/25m |
| Peel Strength(AL) | ASTM-D1000 | 80N/25m |
| 型號Item No. ? | 公稱內(nèi)徑 ? | 收縮前 | After Shrinkage (mm)收縮後 | 包裝 Std.Pkg. M | 適用范圍 | |||
| inch | mm | 內(nèi)徑 D | 最大內(nèi)徑D1 | 總壁厚 | 膠層厚度 | |||
| SCM6-1.2 | 0.236 | Φ6 | 6±0.08 | 1.27 | 1.30±0.15 | 0.56±0.15 | 1.22/支 | 1.27-6 |
| SCM8-1.6 | 0.315 | Φ8 | 8±0.08 | 1.65 | 1.65±0.15 | 0.76±0.15 | 1.22/支 | 1.65-8 |
| SCM12-2.4 | 0.472 | Φ12 | 12±0.08 | 2.41 | 2.00±0.15 | 1.02±0.15 | 1.22/支 | 2.41-12 |
| SCM18-4.4 | 0.708 | Φ18 | 18±0.08 | 4.45 | 2.50±0.15 | 1.37±0.15 | 1.22/支 | 4.45-18 |